Microscopy lab company in the USA 2021? The scan from left to right shows a high tin concentration (green line) while areas of higher lead concentrations (blue line) were not intersected by the line scan. At the interface between the tin/lead solder and copper (red line), there is a mixture of the solder and copper which is the intermetallic layer. The EDS Map provides a nice visual mixture of colors which shows the intermetallic layer while the line scan clearly shows the intermetallic with the elemental graph.
Problem: A client was a manufacturer of beverages, bottled water, and other drinks. They received a customer complaint through one of their distributors, which indicated that a customer had been drinking a bottle of water, and as they neared the bottom of the bottle, found a mysterious white powder floating in the bottom. The customer returned the bottle and complained. The client hoped to identify the powder so they could both satisfy their end customer, as well as identify any potential problems in their manufacturing or bottling process.
An affected floor tile was submitted to determine if the previous mold testing had missed a source on the tile backing or mastic. Additionally, a new tile from the same manufacturing lot was submitted for comparison. The process of preparing and examining the sample and reference tile was documented. Areas with darkened surface features were imaged and then cut out and examined. While the dark spots looked very discrete when examined by eye, under top light polarized microscopy they appeared more diffuse at the outer edges. The darkest areas surrounded what appeared to be particles embedded in the surface.
MicroVision Laboratories, Inc. has been providing businesses, consultants and other testing laboratories with expert microscopy and analytical services since 2003. Our client base covers a broad spectrum of industries including semi-conductors, aerospace, electronics, biomedical, ceramics, optics, pharmaceuticals, mineralogy, metallurgy, thin films, environmental, membranes filtration and industrial hygiene. Discover even more info at Microvision labs.
Do you give lab tours? Yes, we routinely give lab tours to our clients and potential clients. Please call and we would be happy to schedule a tour for you and your co-workers. Do you have other locations around the country? We do work for companies all across the United States, with one laboratory which is located in Chelmsford, Massachusetts. Did MicroVision Labs ever operate under a different company name? No, we have always been MicroVision Laboratories, Inc. Our founder, John Knowles, used to work for another laboratory that underwent several name changes (Eastern Analytical Laboratories, Industrial Environmental Analysts, American Environmental Network, Severn Trent Laboratories, and EMLab P&K Billeria) and was located nearby in Billerica. When that laboratory was closed in 2008, John hired a few of the remaining analysts and acquired its equipment, client list and phone number.
Energy Dispersive X-Ray Spectroscopy (EDS): While in a Scanning Electron Microscope (SEM), samples are exposed to high energy electrons in a vacuum, which generates X-rays through secondary electron transitions. Variations in electron configuration specific to each element generate different energy electrons, and thus different signature energy peaks, indicating which elements are present in the sample. Analysis is performed only on areas which are exposed to the electron beam, facilitating precise control of the analyzed area. This means the composition of very small areas or particles in a sample can be taken. Since EDS is performed in the SEM chamber, a quick and easy interrogation of the surface materials as viewed on the SEM is possible. This can be expanded to include the entire sample, please see our Elemental Mapping page. Additionally, relative amount of the elements present can be calculated, generating composition percentages. Explore a few extra info on this website.